Revista mexicana de física
Print version ISSN 0035-001X
Rev. mex. fis. vol.52 n.4 México Aug. 2006
Investigación
Lamellar ceramics of Ca2SiO4 prepared by mechanical activation of powders
A.B. Cabrera and M.E. Mendoza
Instituto de Física, Universidad Autónoma de Puebla, Apartado Postal J48, Puebla 72570, México.
Recibido el 28 de marzo de 2006
Aceptado el 6 de julio de 2006
Abstract
Stoichiometric mixtures of calcium carbonate and silicon oxide have been mechanically activated by milling during several hours (29 and 50) previous to the solid state reaction, in order to obtain dicalcium silicate, Ca2SiO4. Xray powder diffraction and differential thermal analysis studies show that the mechanical processing of the powders induces changes in the orientational uniformity of crystallites and the diminution of the decomposition temperature of the calcium carbonate. Microlamellar particles of βCa2SiO4 were obtained when the solid state reaction was achieved at 1450°C, whereas βCa2SiO4 and α'LCa2SiO4 phases were obtained when the reaction took place at 1000°C. By means of the powder processing described in this work, we can prepare phase βCa2SiO4 without any chemical stabilizer and with an unusual lamellar morphology.
Keywords: Dicalcium silicate; mechanical activation; lamellar morphology.
Resumen
Mezclas estequiométricas de carbonato de calcio y óxido de silicio fueron activadas mecánicamente mediante molido durante varias horas (29 y 50) antes de la reaccion de estado sólido, con el fin de obtener silicato dicálcico, Ca2SiO4. Los estudios mediante difracción de rayos X en polvos y análisis térmico diferencial muestran que el procesamiento mecánico de los polvos induce cambios en la uniformidad de la orientación de los cristalitos y la disminución de la temperatura de descomposición del carbonato de calcio. Se obtuvieron partículas microlaminares de βCa2SiO4 cuando la reacción en estado sólido se realizó a 1450°C, mientras que cuando la reacción se efectuó a 1000°C, se obtuvo una mezcla de las fases βCa2SiO4 y α'LCa2SiO4. Por medio del procesamiento de los polvos descrito en el presente trabajo, es posible obtener la fase βCa2SiO4 sin ningún estabilizador químico y con una morfología laminar poco usual.
Descriptores: Silicato dicálcico; activación mecánica; morfología laminar.
PACS: 81.20.Ev; 81.05.Je; 61.10.Nz
DESCARGAR ARTÍCULO EN FORMATO PDF
Acknowledgments
We wish to thank to Dr. R. Silva for the SEM photographs. This work was partially supported by CONACyTMexico (Grant C0244296) and VIEPUAP (Grants II 20004/EXG/G and II 143G04). A.B. Cabrera received a scholarship from CONACyTMexico, No. 159190.
References
1. J.G. Fletcher, J.M.S. Skakle, I.R. Gibson, R.I. Smith, and F.P. Glasser, ISIS Experimental report (1997). [ Links ]
2. V.K. Peterson, Ph.D. Thesis, University of Technology, Sydney, Australia, (2003). [ Links ]
3. H. Toraya and S. Yamazaki, Acta Cryst. B 58 (2002) 613. [ Links ]
4. A.M. Neville, Properties of Concrete, 3th edition (Prentice Hall, New York, 1985). [ Links ]
5. M. Miyazaki, S. Yamazaki, K. Sasaki, H. Ishida, and H. Toraya, J. Am. Ceram. Soc. 81 (1998) 1339. [ Links ]
6. S.H. Hong and J.F. Young, J. Am. Ceram. Soc. 82 (1999) 1681. [ Links ]
7. L. Nettleship, J.L. Shull Jr., and W.M. Kriven, J. Eur. Ceram. Soc. 11(1993) 291. [ Links ]
8. K. Sasaki, H. Ishida, Y Okada, and T. Mitsuda, J. Am. Ceram. Soc. 76 (1993) 870. [ Links ]
9. E. Gaffet et al., J. Mater. Chem. 9 (1999) 305. [ Links ]
10. G.B. Schaffer and P.G. McCormick, Appl. Phys. Lett. 55 (1989) 45. [ Links ]
11. N.S. Bell, J. Cesarano III, J.A. Voigt, S.J. Lockwood, and D.B. Dimos, J. Mater. Res. 19 (2004) 1333. [ Links ]
12. V. Berbenni and A. Marini, Z. Naturforsch. 57 b (2002) 859. [ Links ]
13. A.K. Galwey and M.E. Brown, Thermal decomposition of ionic solids (Elsevier, Amsterdam, 1999). [ Links ]
14. A K Galwey and M E Brown, Handbook of thermal analysis and calorimetry, Principles and Practice (Ed. M.E. Brown, Elsevier, Amsterdam, 1998) Vol. 1. [ Links ]
15. Q.S. Shen et al., J. Phys. Chem. B 109 (2005) 18342. [ Links ]
16. J.G.M. van Berkum, A.C. Vermeulen, R. Deles, T.H. de Keijser, and E.J. Mittemeijer, J. Appl. Cryst. 27 (1994) 345. [ Links ]