Relaxation of residual stresses induced by laser shock processing

C. Rubio–González^a*, A. Garnica–Guzmán^b and G. Gómez–Rosas^c

ª Centro de Ingeniería y Desarrollo Industrial, Pie de la cuesta No.702, Desarrollo San Pablo, Queretaro, Qro., 76130, México,Tel: +52(442)2119838, fax: +52(442)2119839, e–mail: crubio@cidesi.mx

^b Instituto Tecnológico de Morelia, Av. Tecnológico 1500, Morelia, Mich. 58120, México.

^c Departamento de Física, Centro Universitario de Ciencias Exactas e Ingenierías, CUCEI.Universidad de Guadalajara, Blvd. Marcelino García Barragán 1421, Guadalajara Jalisco, 44430, México.

Recibido el 27 de mayo de 2008
Aceptado el 20 de abril de 2009

Abstract

The Laser shock processing (LSP) is a new surface treatment technique that induces a compressive residual stress field. This work examines the effect of cyclic loading and temperature on the stability of the stress field induced by LSP on 6061–T6 aluminum samples. Residual stress relaxation due to cyclic loading is reported for different stress amplitudes and temperatures. Due to the cyclic creep effect, the residual stress decreases linearly with the logarithm of the number of cycles, N.

Keywords: Laser shock processing; residual stress relaxation; cyclic loading.

Resumen

El Proceso de Impacto con Laser (LSP) es una técnica novedosa para el tratamiento de superficies que induce campos de esfuerzos residuales de compresión. Este trabajo examina los efectos de cargas cíclicas y el efecto de la temperatura en la estabilidad de los campos de esfuerzos inducidos por la técnica LSP en muestras de aluminio 6061–T6. Se reporta la relajación de esfuerzos residuales debidos a las cargas cíclicas para diferentes amplitudes de esfuerzos y diferentes temperaturas. Debido a los efectos de la fluencia cíclica, los esfuerzos residuales decrecen linealmente con el logaritmo del número de ciclos, N.

Descriptores: Proceso de impacto láser; relajación de esfuerzos residuales; cargas cíclicas.

PACS: 42.62.–b; 42.62.Cf; 81.40.Lm

DESCARGAR ARTÍCULO EN FORMATO PDF

References

1. C. Rubio–González, et al., Mater. Sci. Eng. 386 (2004) 291.        [ Links ]

2. U. Sánchez–Santana, C. Rubio–González, G. Gómez–Rosas , J.L. Ocaña, and C. Molpeceres, 260 (2006) 847.        [ Links ]

3. J.M. Yang Y.C. Her, N. Han, and A. Clauer, Mater. Sci. Eng. A. 298 (2001) 296.        [ Links ]

4. Z Hong and Y. Chengye, Mater. Sci. Eng. A. 257 (1998) 322.        [ Links ]

5. L.W. Tsay, M.C. Young, and C. Chen, Corrosion Science 45 (2003) 1985.        [ Links ]

6. J.E. Rankin, M.R. Hill, and L.A. Hackel, Mater. Sci. Eng. A. 349 (2003) 279.        [ Links ]

7. J.P. Chu, J.M. Rigsbee, G. Banas, and H.E. Elayed–Ali, Mater. Sci. Eng. A. 260 (1999) 260.        [ Links ]

8. P. Peyre and R. Fabbro, 27 (1995) 1213.        [ Links ]

9. K. Ding and L. Ye, J. Mat. Proc. Tech. 178 (2006) 162.        [ Links ]

10. D. Lohe, O. Vohringer, Satibility of residual stresses, in: G. Totten, M. Howes, T. Inoue (Ed.) (Handbook of residual stress and deformation of steel, ASM International 2002).        [ Links ]

11. H. Holtzafel, V. Schulze, O. Vohringer, and E. Macherauch, Mater. Sci. Eng. A. 248 (1998) 9.        [ Links ]

12. W. Zhuang, G. R. Haldford, Int. J. Fatigue 23 (2001) S31.        [ Links ]

13. I Nikitin, B Scholtes, H.J Maier, and I. Altenberger, Scripta Materialia, 50 (2004) 1345.        [ Links ]

14. G. Gómez–Rosas, et al., Applied Surface Science 252 (2005) 883.        [ Links ]

15. C. Rubio–González, et al., Applied Surface Science 525 (2006) 6201.        [ Links ]

16. B.D. Cullity and R.S. Stock , Elements of X–ray diffraction, (Prentice–Hall, 2001).        [ Links ]

17. X'Stress User Manual. (Phillips Analytical, 2002).        [ Links ]