LUNA CERVANTES, M.; HERNANDEZ TORRES, J. and ZAMORA PEREDO, L.. Raman spectroscopic study of the influence of voltage-time on titania growth-fast anodized nanostructures. Rev. mex. fis. [online]. 2019, vol.65, n.5, pp.449-458. Epub Apr 23, 2020. ISSN 0035-001X. https://doi.org/10.31349/revmexfis.65.449.
TiO2 nanotubes were prepared by the anodization process of a set of titanium foils in order to study the influence of time and voltage on the morphology of them under a 1.2 wt % NH4F salt concentration, taking advantage of this percent and remarking the great importance of the oxide growth-dissolution speed with this electrolyte concentration. The anodization process consists of an organic media of ethylene glycol, a voltage from 5 to 30 V for a time period from 1 to 6 hours, a constant potential of 30 V for a time lapse from 10 to 360 minutes and 5 to 480 seconds. All anodized samples are rinsed and annealed to 400 ° C for 3 hours to obtain an anatase crystalline structure. The morphological characterization was carried out by Field Emission Scanning Electron Microscopy (FESEM) to verify the presence of the main nanostructures: nanopores, nanotubes, and nanograss. Raman spectroscopy was used for optical characterization in order to identify the changes in the signal of the E g (v6) vibrational mode. It was observed the Raman E g (v6) vibrational mode suffers a redshift at the initial anodization stage with the contribution of the stress between the substrate-oxide layer and the stoichiometry defects. The diameter and tube length have a strong correlation with the oxide thickness (ascendant slope), moreover, this oxide is compared and related to the Raman intensity of the E g (v6) mode, from this fact, it is easy to define some time periods and a voltage range for each titania nanostructures observed.
Keywords : Titania; nanopores; nanotube; nanograss; Raman spectroscopy; 61.46.Fg; 62.23.-c; 81.07.De; 82.45.Cc; 82.45.Yz..