Carbon nanotubes produced from hexane and ethanol

D. Mendoza^a,*, P. Santiago^b, and E. Reyes Pérez^a

^a Instituto de Investigaciones en Materiales, Universidad Nacional Autonoma de México, Apartado postal 70–360, 04510 Mexico D.F. México.
* Corresponding author: doroteo@servidor.unam.mx

^b Instituto de Física, Universidad Nacional Autónoma de México, Apartado postal 20–364, 01000 México D.F. México.

Recibido el 27 de mayo de 2005
Aceptado el 23 de noviembre de 2005

Abstract

The synthesis of multi–wall carbon nanotubes using hexane or ethanol as the carbon source, hydrogen as the carrier gas, and iron as the catalyst with a thermal chemical vapor deposition method, is reported. It was found that the use of ethanol as the carbon source under low temperature (700° C) gives better results than other liquid precursors in obtaining long and clean carbon nanotubes on quartz substrates.

Keywords: Carbon nanotubes; chemical vapor deposition.

Resumen

En este trabajo se reporta la síntesis de nanotubos de carbono de paredes multiples empleando la técnica de descomposición térmica de vapores. Se emplean hexano y etanol como precursores líquidos para el carbono, se utiliza hidrogeno como gas de arrastre y hierro como catalizador. Se encuentra que la descomposicion de etanol a 700° C sobre sustratos de cuarzo da lugar a nanotubos largos con pocas impurezas.

Descriptores: Nanotubos de carbono; descomposicion térmica de vapores.

PACS: 61.46.fw; 81.16.Be; 81.16.Hc

DESCARGAR ARTICULO EN FORMATO PDF

Acknowledgement

We would like to thank Carlos Flores (IIM–UNAM) for his help in obtaining low magnification TEM images, and L. Rendon (IF–UNAM) for high–resolution TEM.

References

1. R.H. Baughman, A.A. Zakhidov, and W.A. de Heer, Science 297 (2002) 787.        [ Links ]

2. M.S. Dresselhaus, G. Dresselhaus, and Ph. Avouris, Carbon Nanotubes, eds. (Topics in Applied Physics, vol. 80. Springer, Berlin 2001).        [ Links ]

3. K. Hata et al., Science 306 (2004) 1362.        [ Links ]

4. K. Kempa et al., Nano Letters 3 (2003) 13.        [ Links ]

5. P. Wu, B. Kimball, J. Carlson, and D.V.G.L.N. Rao, Phys. Rev. Lett. 93(2004) 013902.        [ Links ]

6. Y. Wang et al.,Appl. Phys. Lett. 86 (2005) 153120.        [ Links ]

7. H.W. Zhu, C.L.Xu,D.H. Wu, B.Q. Wei, R. Vajtai, and P.M. Ajayan, Science 296 (2002) 884.        [ Links ]

8. Y. Li, I.A. Kinloch, A.H. Windle, Science 304 (2004) 276.        [ Links ]

9. L.X. Zheng et al., Nature Materials 3 (2004) 673.        [ Links ]

10. C. Emmenegger et al., Carbon 41 (2003) 539.        [ Links ]

11. S. Murayama, R. Kojima, Y. Miyauchi, S. Chiashi, and M. Cono, Chem. Phys. Lett. 360 (2002) 229.        [ Links ]

12. L. Dong et al., J. Nanosci. Nanotech. 2 (2002) 155.        [ Links ]

13. A.L. Elías et al., Nano Letters 5 (2005) 467.        [ Links ]

14. O.A. Louchev, T. Laude, Y. Sato, and H. Kanda, J. Chem. Phys. 118 (2003) 7622.        [ Links ]

15. A.R. Harutyunyan, T. Tokune, and E. Mora, Appl. Phys. Lett. 87 (2005) 051919.        [ Links ]