LOPEZ-ROMERO, S.    MORALES LEAL, F.. γ-Fe₂O₃/ZnO composite particles prepared by a two step chemical soft method. []. , 57, 3, pp.236-240. ISSN 0035-001X.

^len^aComposite iron oxide-Zinc oxide (γ-Fe₂O₃/ZnO) was synthesized by two step method: in the first one step γ-Fe₂O₃ particles were obtained by a cetyltrimethylammonium hydroxide (CTAOH) assisted hydrothermal method at low temperature (60°C). In the second step, the γ-Fe₂O₃ particles were included in the ZnO particles synthesis, which were obtained by a hexamethylenetetramine (HMTA) assisted hydrothermal method at low temperature (90° C). SEM study of the samples revealed that the γ-Fe₂O₃/ZnO composites present a compact morphology. The γ-Fe₂O₃ and ZnO phases were identified by XRD, energy dispersive X-ray analysis (EDX) and analysis of the IR spectrum. The composite exhibit the characteristic emissions of ZnO under UV radiation and ferromagnetic behavior of γ-Fe₂O₃ under an external magnetic field.^les^aEn este trabajo el compuesto formado entre el óxido de hierro y el óxido de zinc (γ-Fe₂O₃/ZnO) fue sintetizado por el método sol-gel en dos pasos: en el primer paso partículas del óxido de hierro γ-Fe₂O₃ fueron obtenidas por el método hidrotérmico asistido con hidróxido de cetiltrimetilamonio (CTAOH) a baja temperatura (60°C). En el segundo paso, las partículas del óxido γ-Fe₂O₃ fueron incluidas en la síntesis de las partículas de ZnO las cuales fueron obtenidas por el método hidrotérmico asistido con hexametilentetramina HMTA) a una temperatura de 90°C. El análisis SEM de las muestra revele) que las partículas del compuesto γ-Fe₂O₃/ZnO presentan una morfología redonda compacta. Las fases γ-Fe₂O₃ y ZnO fueron identificadas por XRD, análisis de rayos x con energía dispersiva (EDX), y análisis de espectro IR. El compuesto exibe emisión característica del ZnO bajo radiación UV y comportamiento ferromagnético del γ-Fe₂O₃ bajo un campo magnético.

: .

        · | |     · |     · ( pdf )