Introduction
Polystyrene foam is a polymer produced from styrene monomer known as styrofoam; their use in food and electronics packaging, airplane and automotive parts, sporting equipment, among others, it has become a trend last years due to its different advantages as light weight (reduced bulk density), easy to form, low thermal conductivity, and low cost of production (Warsiki et al., 2012; Tsivintzelis et al., 2007). Commercial interest in polymeric foams has been increased due to new emerging applications and the ability to foam a variety of polymeric materials or composites. Despite their success, the continuous growth in research of foamed polymers into new markets depends on the ability to enhance control over its mechanical structure and performance (Emami et al., 2014).
Conventional polymer foaming process usually consist of polymer matrix saturation with a fluid (solvent) and its volatilization by increasing temperature, which induce phase separation, resulting in formation (nucleation) and growth of pores inside the polymer matrix (Tsivintzelis and Panayiotou, 2013). Polystyrene foaming has been extensively studied, for example, recently Nistor et al. (2013) prepared micro-cellular PS foams and studied the influence of toluene residua on the foam structure, using CO2 as high-pressure inductor. They observed that foam heat insulation properties improve with increasing porosity, and that toluene residua increased the porosity by increasing the cell sizes and lowering the thickness of the compact skin at the film surface. Gutiérrez et al. (2014), foamed polystyrene using limonene solutions as solvent and CO2 as foaming agent. They studied the effect of pressure, temperature, concentration of the solution, contact time and vent time over the diameter of cells, its standard deviation and the cells density, observing that the most suitable conditions to foam polystyrene from limonene solutions were 90 bar, 30°C, 0.1 g of Polystyrene/ml limonene, 240 min contacting and 30 min venting. Thus, foaming process strongly depends on solvent type and how temperature is raised. Usually, natural gas or fossil fuels are used in this process. However, constant increase in their prices and the pollution factor leads to finding new and clean (non-toxic) manufacturing techniques. Electromagnetic waves ranging from radiofrequency to microwaves could be an efficient alternative option for processes involving heating increase in polymers (Mallakpour and Rafiee, 2011). Sen et al. (2011), used microwave irradiation as the source of energy for expansion process and 2-propanol as expansion agent, however, they did not studied the thermal effects which have a direct impact in the quality of the product.
This work present thermal characterization profile of EPS manufacturing using microwaves as the source of heating throughout polystyrene foaming, and using ethanol, a mixture of ethanol/water and hydrogen peroxide as expansion agents. Advantages of this method includes fast heating, low-cost process, and independence of fossil fuels.
Methods and procedures
In order to characterize thermal profile, experimental and numerical simulations using Comsol Multiphysics® were performed.
Experimental foaming process
Samples of 130 ml commercial expandable polystyrene with a density of 20 kg/m3 and thermal conductivity of 0.35 W/m∙K were utilized. To increase the radiation absorption, experiments in conjunction with three solvents: ethanol, a mixture 25:75 wt./wt. of water/ ethanol and hydrogen peroxide were performed. Purity of ethanol utilized was 96%. Solvents were applied directly to pre-expanded EPS beads with a syringe. After that, samples were heated for 180 seconds into a commercial microwave oven with maximal power P = 950 W and frequency f = 2.45 GHz as shown in Figure 1a. In order to determinate thermal distribution, measurements of foamed material were performed using an infrared laser measurer fabricated by Extech Instruments model 42510A. Temperature measurements were taken at the center, top, bottom and lateral side (Figure 1b).
Mathematical modeling and simulation
Since EPS is transparent to microwave wavelength, a heat transfer mechanism is required. Polar molecules as water present favorable conditions to be heated when they are irradiated by microwave. Eq. (1) and (2) describe the process of microwave heating (Warren et al., 2012).
From eq. (1)
ρd = material density
Cp = specific heat at a given temperature
k = thermal conductivity
qabs = absorbed volumetric power density
From eq. (2)
w = angular frequency
ε" eff = (s/ωε0) = imaginary part of the complex permittivity from the material which is also known as loss tangent (tgδ)
σ = material conductivity
ε0= free space permittivity
E = electric field
Steam produced above boiling point allows thermal energy transfer to the materials such as polystyrene to achieve thermal expansion required for its manufacturing process. The property that determines the absorption of electric field produced by microwave and its conversion to heat is the complex dielectric constant. This parameter is composed by the dielectric constant of the material that represents the capacity to store electric charge, and the loss tangent (tgδ), which is the absorption level of radiation that is transformed to heat. Table 1 shows microwave absorption of some solvents (Shadpour, 2011). It is observed that water provides a medium absorption level. Hence, uses of solvents of high loss tangent are expected to be more efficient for EPS manufacturing with microwave.
In order to estimate the response time and 3D thermal distribution simulations were performed in the software COMSOL Multiphysics 4.3. Parameters utilized are shown in Table 2.
From Table 2, the value of electric conductivity is cero since EPS is a dielectric material. Relative permittivity is a complex number where the real part represents the dielectric constant of material and the complex number means material absorption or loss tangent which is in the range of 5x10-7 to 5x10-3 (Jerzy et al., 1998). Relative permeability of 1 means that the material is not affected by magnetic fields. Thermal conductivity is the quantity of heat transmitted through a unit thickness in a direction normal to a surface of unit area, due to a unit temperature gradient. According to Askeland (2001) its value for foam polystyrene is 0.029. Density is the material mass per unit volume, its from 10 to 50 kg/m3 (EPS, 2003). Finally, heat capacity is the amount of heat needed to raise the temperature of the system by one degree. For expanded polystyrene its value is 1210 J/(kg*K) (Incropera and DeWitt, 1999).
Results and discussion
Experimental results of EPS fabrication using solvents
In order to study the repeatability of manufacturing process, each experiment was made six times. Obtained results of EPS mixed with ethanol, below 120 seconds of microwave heating presented expansion as required in the manufacturing process. However, moisture was also present which is undesirable. At 150 seconds, humidity was eliminated, but the material presented easy detachment of polystyrene pearls. At 180 seconds of microwave radiation, only small detachment on the top of material was observed (Figure 2a). Tests were also performed for a mixture of water/ ethanol with a volume ratio of 4:3. In the range of 120 to 180 seconds humidity and material detachment was observed (Figure 2b).
Better results were achieved when hydrogen peroxide was used as solvent. In this case, at 180 seconds, expanded EPS did not present detachment, nor humidity (Figure 3).
Due favorable results achieved with hydrogen peroxide, quantitative studies were performed in this particular case. Experimental thermal distributions of EPS at top, bottom, center and lateral side after microwave heating with hydrogen peroxide are shown in Figure 4. Results showed an accuracy of ±6 °C at top, bottom and lateral sides. However, accuracy at center was ±23 °C.
Numerical simulation results
Result of numerical simulation performed in COMSOL Multiphysics solving eqs. (1) and (2) is shown in Figure 5. Input parameters utilized were: f = 2.45 GHz, t = 180 s and ε = 2.7-141x10-6 j. As it can be seen from Figure 5, simulated thermal distribution varies in a range of 21°C. Theoretically, this is mostly originated by the electric field distribution of microwaves. Simulations behavior on top sections of lateral sides showed agreement with experimental results in the range of 45 to 52 °C.
Thermal distribution shown in Figure 6 corresponds to a final time of simulation at 180 seconds. The evolution of temperature with respect to time is depicted in Figure 6. Initial condition of temperature was 25 °C. As it can be seen from Figure 6, increase of temperature is exponential below 80 s. From 80 to 180 seconds temperature behavior is linear with a slope of 0.14.
Discussion of results
Experimental results showed that the use of ethanol as solvent for heating EPS with microwaves in spite of a fast increase in temperature, it produces moisture or easy detachment of pearls in EPS which could represent an issue in industrial processes. The same problem was observed for mixture of ethanol and water. Moisture problem can be solved increasing time exposure to microwaves from 180 to 300 seconds. However, this represent an increase of 60% of kWh which also represents an increase in cost production. In the other hand, the use of hydrogen peroxide showed elimination of moisture and lack of detachment of EPS. Numerical simulations showed a temperature range on the system (EPS and solvents) from 45 to 65 °C, whereas experimental results showed an overall range from 46 to 80 °C. This variation may be associated with the conditions of measurements at the center of the material. In this case temperatures were taken by destructive tests. On the other hand, measurements in lateral sides, top, and bottom are more uniform as can be seen in Figure 4.
Conclusions
Fabrication of EPS with microwaves at 2.45 GHz and three different solvents, i.e. ethanol, hydrogen peroxide and a mixture of water/ethanol were demonstrated. The better result was achieved with hydrogen peroxide. Elimination of moisture and solid EPS fabrication was observed for 180 seconds of manufacturing process. Simulation and experimental results showed non-uniform thermal distribution, which depends of microwave wavelength, and the electrical field distribution. Future studies could include the implementation of longer wavelengths to attenuate temperature variations. This work could potentially benefit polystyrene manufacturing industry, specifically in energy and time saving.