SECUNDINO-SANCHEZ, O.; DIAZ-REYES, J.; SANCHEZ-RAMIREZ, J.F.  y  JIMENEZ-PEREZ, J.L.. Structural and optical characterization of the crystalline phase transformation of electrospinning TiO₂ nanofibres by high temperatures annealing. Rev. mex. fis. [online]. 2019, vol.65, n.5, pp.459-467.  Epub 23-Abr-2020. ISSN 0035-001X.  https://doi.org/10.31349/revmexfis.65.459.

The electrospinning technique has been used to synthesize TiO2 nanofibres, which by annealing at high temperatures achieves the crystalline phase transformation of anatase to rutile passing through the anatase-rutile mixed. The investigated temperature range was 0-1000 ° C. The TiO2 nanofibres surface morphology and chemical stoichiometry were obtained by Scanning Electron Microscopy and Energy Dispersive Spectrometry. The annealed nanofibres diameter was ranged from 137.0 to 115.3 nm in the investigated temperature range. The influence of the annealing temperature on the structure and crystalline phase quality of the TiO2 nanofibres has been investigated by X-ray diffraction and Raman scattering. Clear evidence have been obtained of the structural transformation of TiO2 nanofibres from pure anatase to pure rutile, including the almost amorphous and anatase-rutile mixed structural phases by X-ray diffraction and confirmed by Raman scattering. By X-ray diffraction was found that the TiO2 nanofibres crystalline phases presented as preferential growth direction (101) for anatase and (110) for rutile. The Raman spectroscopy exhibits the anomalous behavior for band broadening and shifting of Raman bands with increasing crystallite size that forms the nanofibres. The room-temperature photoluminescence presents radiative bands whose dominant band redshifts from 2.56 to 1.32 eV, as the crystalline phase is transformed by annealing at high temperature.

Palabras llave : Electrospinning technique; semiconductor nanofibres; titanium dioxide; structural properties; Raman spectroscopy; X-ray diffraction; 61.05.cp; 61.43.Dq; 61.46.Hk; 61.66.Fn; 61.72.jd; 61.72.jj; 63.22.Gh; 68.55.ag; 78.67.Lt.

        · resumen en Español     · texto en Inglés     · Inglés ( pdf )