SOLIS, J.L; RODRIGUEZ, J  e  ESTRADA, W. Highly porous tungsten-oxide-based films obtained by spray-gel for gas sensing applications. Rev. mex. fis. [online]. 2006, vol.52, suppl.2, pp.29-31. ISSN 0035-001X.

Highly porous mixed WO₃-SnO₂ films have been prepared from an aqueous solution of SnCl₄.5H₂O and polytungsten gel with a molar ratio of Sn/W from 0 to 1. These solutions were sprayed on to alumina substrates at 220°C. The obtained films were annealed at 600°C in air for 3 h. The annealed films were composed of a mixture of WO₃ and SnO₂ phases. The gas sensitivity to butanol and ethanol vapors is enhanced when the Sn/W molar ratio increases in the film by up to 0.1, with further increments to this proportion the sensitivity decreases.

Palavras-chave : Tungsten oxide; tin oxide; gas sensor; pyrolysis.