vol.67 número6Structural and thermodynamic properties for the BaMn(Fe/V)F 7 fluoride glass system by using the Hybrid Reverse Monte Carlo simulationPredictive study of ferromagnetism and antiferromagnetism coexistence in Ba1-xGdxRuO3 induced by Gd-doping índice de autoresíndice de materiabúsqueda de artículos
Home Pagelista alfabética de revistas  

Servicios Personalizados

Revista

Articulo

Indicadores

Links relacionados

  • No hay artículos similaresSimilares en SciELO

Compartir


Revista mexicana de física

versión impresa ISSN 0035-001X

Rev. mex. fis. vol.67 no.6 México nov./dic. 2021  Epub 14-Mar-2022

https://doi.org/10.31349/revmexfis.67.061003 

Research

Material Sciences

DFT and TB-mBJLDA studies of structural, electronic and optical properties of Hg1-xCdxTe and Hg1-xZnxTe

N. Aouail1 

M. Noureddine Belkaid1 

A. Oukebdane1 

M. Hocine Tedjini1 

1Laboratory for Analysis and Application of Radiation, Department of Physics, Faculty of Physics, University of Sciences and Technology of Oran Mohamed Boudiaf, BP1505 ElMenaouer, Oran31000, Algeria. e-mail: nouria.aouail@gmail.com; mnbelkaid@gmail.com; oazizdz@yahoo.com; tedjini.mohammedhocine@gmail.com


Abstract

In this paper, the fundamental semiconductor properties of Hg1-xCdxTe and Hg1-xZnxTe are investigated by ab initio calculations based on the FPLAPW method. Structural properties have been calculated using LDA and GGA approximations. The electronic properties are studied using the LDA and GGA approximations and the potential TB-mBJLDA coupled with the lattice parameters aLDA and aGGA. The optical properties are determined from the optimal gap energies based on the TB-mBJLDA potential. Lattice parameters aLDA obtained by the LDA calculations predict values that are in good agreement with the experimental results and are better than those results obtained by the GGA calculations. The use of TB-mBJLDA potential coupled with the lattice parameter aGGA gives gap energy values in good agreement with the experimental results for all alloys except Hg1-xZnxTe (x = 0.5,0.75) where the (TB-mBJLDA+aLDA) is more suitable. Optical constants are calculated from the dielectric function in the energy range (0-30 eV). The spectrum of real and imaginary parts of the dielectric function, the energy loss function, the refractive index, the extinction coefficient, the absorption coefficient, and the reflectivity show that optical properties of Hg1-xCdxTe are comparable to those of Hg1-xZnxTe. Our results are found to be in reasonable agreement with existing data reported in the literature.

Keywords: Ab initio; FPLAPW; TB-mBJLDA; gap energy; optical properties

PACS: 42.70.-a; 31.15.Ar; 61.82.Fk; 71.15.Mb; 71.20.-b; 73.20.At

1.Introduction

Mercury-cadmium telluride Hg1-xCdxTe and Mercury-Zinc Telluride Hg1-xZnxTe are two competitive materials used in infrared radiation detection 1,2. They have important applications in medicine and biology (laser IR, infrared camera) 3, in the industry (control of food products, rubber industry...) 4,5, and security (surveillance in military fields) 6. They are also used as Solar cells and photo-conductors 2-7-8. These are pseudo-binary semiconductors in the (II-VI) groups with small gaps and the same structural properties 9,10. The gap energies of the Hg1-xCdxTe alloys are between - 0.3 eV (HgTe) and 1.6 eV (CdTe) and fall within the infrared radiation energy range (IR) [ E ≤ 1.65eV]. However, the Hg1-xZnxTe possesses gap energies from -0.3 eV (HgTe) to 2.38 eV (ZnTe) and mechanical hardness that is greater than those of the Hg1-xCdxTe. These alloys are found to have the same nature of gaps 11,12.

Recently, M. Debbarma et al.,13 investigated the elastic and thermal properties of zinc Blende Hg1-xCdxTe ternary alloys using the FP-LAPW method. F. Kadari et al.,14 used WIEN2K code to study the structural properties of Hg1-xCdxTe and Hg1-xZnxTe alloys and the electronic properties of Hg1-xCdxTe and Hg1-xZnxTe alloys for X = 0.5 within the PBE-GGA and WC-GGA approximations in the zinc blende structure. The TB-mBJGGA potential combined with the PBE-GGA approximation was again used to study the electronic properties of the same materials. The results obtained are in agreement with experimental data. A. Laref et al.,15 studied the electronic structure, and optical characteristics of ZnHgTe alloys at concentrations x=0.25, 0.50, 0.75 by using the mBJ-GGA approach S. Al-Rajoub and B. Hamad 16 have studied the structural, electronic, and optical properties of the ternary alloy (X = 0.0, 0.25, 0.5 and 0.75), using WIEN2K code. In the same study, calculations of the structural properties are carried out with the LDA and GGA approximations for X = 0.0, 0.25, and 0.75 in the zinc blende structure and the tetragonal structure for X = 0.5. However, the electronic properties are determined with different approximations, namely: LDA, GGA, (LDA/GGA) + U, and (LDA / GGA) +mBJ. The mBJ+GGA approach gives better results for the electronic properties, except in the case of HgTe, where the GGA+U is better. The dielectric function was calculated using data obtained from the approximations giving the best gap values. B.V. Robouch et al 17 presented experimental results of the optical properties (dielectric function and reflectivity) of Hg1-xCdxTe and Hg1-xZnxTe for different concentrations. To our knowledge, there are no results published on the optical properties of Hg1-xZnxTe alloys for X = 0.25, 0.5, and 0.75 except Laref et al., 15. Moreover, there are no published results on the absorption spectrum of Hg1-xCdxTe, the refractive, and the reflection indexes of Hg1-xCdxTe (X=0.25, 0.75). Our contribution to the research topic is the use of two theoretical approaches, namely, the DFT and TB-mBJLDA for a detailed investigation of electronic and optical properties. To show the importance of the lattice parameter values in the computation of gap energy, the lattice parameter optimized either by LDA or GGA approximation has been used as an input parameter of the ‘TB-mBJLDA’ approach. As for the optical properties, a more comprehensive study and a detailed analysis of the optical coefficients, namely, the absorption spectrum, the refractive, and reflectivity index has been carried out an aspect that has found little interest in the published theoretical results in the literature.

The DFT is known for its underestimation of the gap energy 18, which has a direct impact on the computation of physical properties that are functions of gap energy, namely the linear optical properties 14. The option of using the DFT combined with the TB-mBJLDA potential 19 is considered, knowing that small variations of the lattice parameter values may generate important variations in the gap energy 20. In this work, the DFT (LDA and GGA) is used for the optimization of the lattice parameter of Hg1-xCdxTe and Hg1-xZnxTe for X = 0.0, 0.25, 0.5, 0.75, and 1.0. A comparative study of the electronic properties of these materials is carried out. It consists in performing a series of ab-initio calculations (LDA and GGA) with and without the TB-mBJLDA potential. Previous work using the TB-mBJLDA 21 has proved that the approach is successful for determining electronic and optical properties. Results from the first principle calculations are used to compute optical properties of Hg1-xCdxTe and Hg1-xZnxTe alloys in the zinc-blende structure at concentrations X in the range (0,1). The determination of the dielectric function will use data based on the approach giving the best gap energy. Our objective is to complete previous theoretical works regarding the structural, electronic, and mainly optical properties of Hg1-xCdxTe and Hg1-xZnxTe alloys for different values of X. In the following, the methodology is exposed, followed by an analysis of the obtained results and a conclusion.

2.Computational details

The method used in this work is the self-consistent full-potential linearized augmented plane wave (FP-LAPW) 22 as implemented in the ELK code 23, within the limits of LDA 24 and GGA 25 approximations. The study is concerned with the stability of HgTe, CdTe, ZnTe materials, and their ternary alloys Hg1-xCdxTe and Hg1-xZnxTe with concentrations X = 0.25, 0.5, 0.75, in the zinc blende structure.

The used values of muffin-Tin sphere radii (RMT) in (u.a) are 2.62 for (Hg and Cd) and 2.42 for (Zn and Te). The K points grid in the Brillouin zone is chosen to be 14 x 14 x 14 and the maximum length of (G+K) vectors is fixed so that 8.0/RMT=1 a.u-1. The self-consistency calculation is stopped when the difference between two successive total energy values is less than 10-6.

Besides the use of LDA and GGA approximations, the study of electronic properties has required the use of the Tran-Blaha modified Becke-Johnson+LDA potential (TB-mBJLDA) 26, whose formulation is given by:

uM B Jx,σ(r)=cuBRx,σ(r)+(3c-2)1π5122tσ(r)nσ(r), (1)

where c, is the added parameter by Tran and Blaha to the mBJ potential, uBRx,σ is the Becke-Rousseln potential, tσ(r) and nσ(r) represent, respectively, the kinetic energy and the electronic densities that are functions of spin. The TB-mBJLDA potential, whose mBJ exchange potential is available in the library interface LIBXC 27, is used in combination with the lattice parameters optimized by the LDA or GGA approximations.

Optical properties were studied using the TB-mBJLDA approximation and a choice of lattice parameter values that guarantee the best gap energies in the range (0-24 eV).

3.Results and discussion

3.1.Structural properties

The equilibrium lattice parameter, the bulk modulus, and the derivative of the bulk modulus of the chosen materials are determined in the zinc blende structure where the binary alloys have the F-43m (2 1 6) space group, where Cd, Zn, or Hg atoms occupy the (0,0,0) position, and Te occupy the (0.25,0.25,0.25); however, the ternary alloys Hg1-xCdxTe and Hg1-xZnxTe (x = 0.25,0,5 and x = 0.75) are the results of the injection of Cd or Zn atoms in the unit cell of HgTe. The atomic positions of the different atoms and the different concentrations are reported in Table I; however, the crystal structures are shown in Fig. 1. The variation of the total energy as a function of the lattice volume of each alloy has been represented in the ET-lattice parameter (a) plane. The analytical expressions of these variations have been obtained by the Birch-Murnaghan 28 fit, whose equation of state is:

E(V)=E0+98B0V0V0V2/3-12+916B0(B-0'-4)V0V0V2/3-13. (2)

Figure 1 Geometrical structures of Hg 1-x Cd x Te and Hg 1-x Zn x Te (x = 0:25, 0.5, and 0.75). 

Table I Atomic positions of Hg 1-x Cd x Te and Hg1-x Zn x Te: ternary alloys. 

X Atomes Positions
0.25 Hg (0, 0, 0), (0.5, 0, 0.5), (0.5, 0.5, 0)
Cd or Zn (0, 0.5, 0.5)
Te (0.25, 0.25, 0.25), (0.75, 0.75, 0.25), (0.75, 0.25, 0.75), (0.25, 0.75, 0.75)
0.5 Hg (0, 0, 0), (0.5, 0.5, 0)
Cd or Zn (0.5, 0, 0.5), (0, 0.5, 0.5)
Te (0.25, 0.25, 0.25), (0.75, 0.75, 0.25), (0.75, 0.25, 0.75), (0.25, 0.75, 0.75)
0.75 Hg (0, 0, 0)
Cd or Zn (0.5, 0, 0.5), (0.5, 0.5, 0), (0, 0.5, 0.5)
Te (0.25, 0.25, 0.25), (0.75, 0.75, 0.25), (0.75, 0.25, 0.75), (0.25, 0.75, 0.75)

Table II shows the structural properties of the binary materials: HgTe, CdTe, and ZnTe, which are compared with the available theoretical and experimental data. The lattice parameters obtained by the LDA approximation are close to the experimental values. However, those obtained by the GGA approximation are overestimated. The lattice parameters of HgTe, CdTe, and ZnTe are in good agreement with the theoretical 11-14-16-42 and experimental data 45-57-58-60. LDA calculations underestimate values of the lattice constants of HgTe, CdTe and, ZnTe, by about 0.23% (HgTe),0.10% (CdTe), and 1.78% (ZnTe) when compared to the experimental values of 6.46 A, 6.48 A, and 6,10 A17-43-45. However, GGA calculations overestimate values of the lattice constants of HgTe, CdTe and, ZnTe, by about 3.09% (HgTe), 3.9% (CdTe), and 1.29% (ZnTe) when compared to the experimental values 17-43-45. Values of the bulk modulus calculated by GGA are smaller than those values found by LDA approximation which are in good agreement with theoretical 11-14,42 and experimental data 59,51,45. Among the different compounds, it is found that ZnTe has the largest value of bulk modulus (53.09 GPa).

Table II Optimized lattice constant (a), bulk modulus (B) and bulk modulus derivative B´ of HgTe, CdTe, and ZnTe in zinc blende structure. 

Parameter This work Other works
Theoretical Experimental
LDA GGA 6.453d, 6.461g
HgTe a (Å) 6.445 6.66 6.644a, 6.6385b, 6.458c
B (Gpa) 46,3 32.35 35.57b 42.3i
B’ 5.85 5.78 5.494b
CdTe a (Å) 6,487 6,734 6.421c, 6.614b, 6.42m 6.467h, 6.48e
B (Gpa) 41,91 35,15 42.12b, 44.41m 42.4l
B’ 4.90 3.41 4.99b 6.40l
ZnTe a (Å) 5,997 6,179 6.174b, 5.98f, 5.99m 6.009l, 6.103j
B (Gpa) 53.09 41,182 52.21f , 51.62m 51l, 50.50k
B’ 4.80 4.86 4.86f 4.7l, 5.00k

a Ref. 16, b Ref. 14, c Ref. 37, d Ref. 57, e Ref. 43, f Ref. 11, g Ref. 17, h Ref. 58, i Ref. 59, j Ref. 60, k Ref. 51, l Ref. 45, m Ref. 42.

Results of the optimized equilibrium lattice constant and bulk modulus of Hg1-xZnxTe and Hg1-xCdxTe, obtained by GGA and LDA approximations for various x concentrations, are listed in Table III. For the lattice parameter, it is found that data relative to Hg1-xZnxTe and Hg1-xCdxTe alloys are in agreement with the theoretical and experimental results 14-17-44-58. It is observed that an increase in the composition X results in a lattice parameter increase. To the best of our knowledge, there are no bulk modulus experimental data available in the literature for Hg1-xZnxTe and Hg1-xCdxTe alloys in the range of X= 0.25 to X = 0.75. Figure 2 shows the plot of the lattice parameter of Hg1-xZnxTe and Hg1-xCdxTe alloys as a function of concentration X, as calculated by LDA and GGA approximations. It is found that an increase in the concentration x results in a nonlinear variation of the lattice parameter.

Figure 2 Lattice parameter variation of Hg 1-x Cd x Te and Hg 1-x Zn x Te alloys as a function of concentration x (LDA and GGA approximations). 

Table III Optimized lattice constant (a), bulk modulus (B) and bulk modulus derivative B´ of ternary alloys Hg1-xCdxTe and Hg1-xZnxTe in zinc blende structure. 

Parameter This work Other works
x LDA GGA Theoretical Experimental
a (Å) 6.432 6,651 6.434a 6.485d
x = 0.25 B (Gpa) 46.77 34.26
B’ 5.96 4.58
a (Å) 6,419 6,643 6.6281b 6.478d
Hg1−xCdxTe x = 0.50 B (Gpa) 46,62 33.09 35.07b
B’ 6.19 4.79 4.96b
a (Å) 6,413 6,625 6.416a 6.473d
x = 0.75 B (Gpa) 48.38 34.12
B’ 5.18 5.10
a (Å) 6,380 6,590 6.37075c
x = 0.25 B (Gpa) 49.56 36.03
B’ 4.70 4.57
a (Å) 6,292 6.475 6.328b 6.2805c
Hg1−xZnxTe x = 50 B (Gpa) 51.18 41.03 37.85b
B’ 4.83 4.85 4.765b
a (Å) 6,224 6,380 6.1902c
x = 0.75 B (Gpa) 54.91 42,35
B’ 4.21 4.44

a Ref. 17, b Ref. 14, c Ref. 44, d Ref. 58.

3.2.Electronic properties

LDA and GGA approximations are used to compute the band structure of HgTe, CdTe, ZnTe, and their ternary alloys based on Hg. The gap energies obtained from the band structure as well as other theoretical (DFT) and experimental results are reported in Table IV and plotted in Fig.3. Good agreement is observed between our results and the available theoretical data 11-14-16-42 and far from agreeing with experimental results 10-54-55-56. The under-estimation of gap energy is one of the problems associated with the use of the DFT (LDA or GGA) while studying electronic properties 18. Despite the fact of being in good agreement with other theoretical (DFT) studies, the values of band gaps of HgTe, CdTe, and ZnTe materials differ from the experimental values. Band gaps associated with the ternary alloys Hg1-xCdxTe and Hg 1-x Zn x Te are found experimentally to have low values. In this work, the DFT calculations give very low gap values for X = 0.75 and even negative values for X = 0.25 and 0.5. For Hg0.25Cd0.75Te, the values of gap energy agree with theoretical data 16,37 and differ slightly for Hg0.75Cd0.25Te and Hg0.5Cd0.5Te compounds. For Hg0.5Zn0.5Te, the values of gap energy are different from those reported in , which use the PBE-GGA approximation. To the best of the author’s knowledge, no theoretical (DFT) results regarding the gap energies of the band gaps of at X = 0.25 and X = 0.75 are found in the literature.

Figure 3 Gap energy variation of Hg 1-x Cd x Te and Hg 1-x Zn x Te alloys as function of concentration x (LDA, GGA + TB-mBJLDA and experimental data). 

Table IV Gap energy values for binary and ternary alloys of Hg 1-x Cd x Te and Hg 1-x ZnxTe alloys for (x = 0:0, 0.25, 0.5, 0.75 and 1), using LDA and GGA approximations. 

Alloys Material This works Other works
Approximation Gap energy (eV) Gap nature Theoretical (DFT) Experimental
HgTe LDA −0.9074 −0.907c −0.3b
binary CdTe GGA LDA −0.9318 0.501 direct Γ − Γ 0.59a, 0.48i 1.606g
GGA 0.425 direct Γ − Γ
ZnTe LDA 1.2661 direct Γ − Γ 1.09a, 1.22i 2.38g
x = 0.25 GGA LDA 1.05264 −0.5241 direct Γ − Γ 0.0f 0.22h
GGA −0.5579
Hg1−xCdxTe x = 0.5 LDA −0.1576 0.0c 0.592h
GGA −0.1997
x = 0.75 LDA 0.21439 direct Γ − Γ 0.203c 1.06h
Ternary x = 0.25 GGA LDA 0.17872 −0.51398 direct Γ − Γ 0.380e
GGA −0.5759
Hg 1-x Zn x Te x =0.5 LDA −0:0765 0.24d 0.990e
GGA −0:3421
x =0.75 LDA 0.3922 direct Γ - Γ 1.621e
GGA 0.3214 direct Γ − Γ

a Ref. 11, b Ref. 56, c Ref. 16, d Ref. 14. e Ref. 10, f Ref. 37, g Ref. 54, h Ref. 55, i Ref. 42.

The same study has been extended to compute the band structure by using the Tran and Blaha modified Becke-Johnson potential (TB-mBJ) coupled with the LDA approximation and the insertion of the lattice parameters that have been optimized either by LDA or GGA approaches. The new gap energy values are reported in Table V. Comparison of the electronic properties data leads to ascertain that good agreement is observed between our results and other theoretical studies 14-16,29,15 for Hg 1-x Cd x Te and Hg 1-x ZnxTe alloys for (X = 0,0.25, 0.5, 0.75, and 1.0).

Table V Gap energy values of binary and ternary alloys of Hg 1-x Cd x Te and Hg 1-x Zn x Te alloys (x = 0:0, 0.25, 0.5, 0.75, and 1), using TB-mBJLDA potential. 

Material This work Otherworks
Allaoys Latticeparameter Gap energy (eV) Gap nature Theoretical (mBJ or GW) Experimental
Binary Hg 1-x Cd x Te HgTe aLDA −0.01968 −0.701a, −0.03e, −0.3h
CdTe aGGA −0.1649 −0.1f, −0.1g
aLDA 1.8137 direct Γ − Γ 1.541c, 1.57e 1.606i
aGGA 1.5273 direct Γ − Γ
ZnTe aLDA 2.6981 direct Γ − Γ 2.138c, 2.33f, 2.38i
aGGA 2.3253 direct Γ − Γ 2.2g
x = 0.25 aLDA 0.4675 direct Γ − Γ 0.39a, 0.22e 0.22b
aGGA 0.2670 direct Γ − Γ
x = 0.5 aLDA 0,892 direct Γ − Γ 0.81a, 0.62e 0.592b
Tenary aGGA 0.678 direct Γ − Γ
x = 0.75 aLDA 1,3486 direct Γ − Γ 1.27a 1.06b
Hg 1-x Zn x Te aGGA 1.1360 direct Γ − Γ
x = 0.25 aLDA 0,5364 direct Γ − Γ 0.29c 0.380d
aGGA 0.3182 direct Γ − Γ
x = 0.5 aLDA 1.0729 direct Γ − Γ 0.773c, 0.72g 0.990d
aGGA 0.8526 direct Γ − Γ
x = 0.75 aLDA 1.6410 direct Γ − Γ 1.58c, 1.35g 1.621d
aGGA 1.4266 direct Γ − Γ

a Ref. 16, b Ref. 55, c Ref. 14, d Ref. 10, e ref. 29. f Ref. 50, g Ref. 15, h Ref56, i Ref. 54.

The gap energy values obtained using the (TB-mBJLDA) approach are, generally, in agreement with the experimental results, which are plotted in Fig. 3, representing a clear improvement when compared to the simple DFT (LDA, GGA) results. Given that the gap energy value is very sensitive to small variations in the lattice parameter values, the use of aGGA instead of aLDA in the computation of gap energy of the binary materials HgTe, CdTe, and ZnTe lead to results that are comparable to the experimental data. The same observation is valid for the ternary Hg 1-x Cd x Te. However, for Hg 1-x Zn x Te, the best gap energies are obtained with aGGA for Hg0.75Zn0.25Te alloy and with aLDA for Hg0.5Zn0.5Te and Hg0.25Zn0.75Te alloys. Figure 4 shows the calculated electronic band structures of the binary materials: HgTe, CdTe, and ZnTe. The valence band maximum (VBMa) and the conduction band minimum (CBMi) for the considered compounds are located at Γ point. The band gap being direct and located at Γ- Γ. Figure 5 shows plots of the energy bands as calculated with the TB-mBJLDA for Hg 1-x Cd x Te. An almost linear increase of the gap energy is observed with increasing Cd concentrations (0.25 to 0.75). Hence, these alloys can be considered semiconductors with direct band gaps at the Γ-point. Plots of the electronic band structure of Hg0.5Zn0.5Te, for x = 0.25 to 0.75, using TB-mBJLDA correction are shown in Fig. 6. An increasing trend of the energy gap is observed with an increasing X.

Figure 4 Band structure of HgTe, CdTe, and ZnTe using TB-mBJLDA potential and aGGA lattice parameters. 

Figure 5 Band structure of Hg 1-x Cd x Te alloy (x = 0:25, 5, and x = 0:75), using TB-mBJLDA and aGGA lattice parameters. 

Figure 6 Band structure of Hg 1-x Zn x Te alloy using TB-mBJLDA and aGGA for x = 0:25, and aLDA for x = 0:5 and 0.75. 

3.3.Optical properties

The complex dielectric function is the starting point for the computation of the optical properties of different materials. These functions are completely determined by the band structures of the considered materials. Hence, knowledge of the complex dielectric function ε(ω) is capable of characterizing the optical response of all materials when subjected to an electromagnetic wave flux 30.

ε(ω)=ε1(ω)+iε2(ω), (3)

ε1(ω) and ε2(ω) are, respectively, the real and imaginary parts of the dielectric function and ω is the angular frequency. The study covers frequencies corresponding to the energy range [0-24 eV]. Optical constants expressions such as the refractive index n(ω), the extinction coefficient k(ω), the energy loss function L(ω), the absorption coefficient (attenuation) α(ω), and the reflectivity R(ω) are expressed in terms of ε1(ω) and ε2(ω) 31-32-33 as follows:

n(ω)=12ε12(ω)+ε22(ω)+ε1(ω)1/2, (4)

k(ω)=12ε12(ω)+ε22(ω)-ε1(ω)1/2, (5)

L(ω)=ε2(ω)(ε12(ω)+ε22(ω)) (6)

α(ω)=2ωck(ω)=2ωcε12(ω)+ε22(ω)-ε1(ω)1/2, (7)

R(ω)=(n-1)2+k2(n+1)2+k2. (8)

In Fig. 7 and 8, the spectrums of the real and imaginary parts of the dielectric function are represented. They summarize the optical processes resulting from the interaction of an electromagnetic wave with a given material. Each material exhibits a Mie resonance when ε11 and ε21, and a metallic character when ε1(ω)<0. Plasmon resonance is observed when ε1<0 and ε21. The peaks in the imaginary part spectrum match the inter-band transition 34-35. The semi-metal HgTe possesses a Mie resonance in the range mid-infrared- short-wave infrared (MWIR-SWIR) and a Plasmon resonance in the ultraviolet (UV). In the energy ranges (4.15 -4.49 eV) and (6.15 - 14.57 eV), ε1(ω) becomes negative. The first and main peaks of ε2(ω) fall, respectively, at energies 0.15 eV and 2.30 eV. A Mie resonance is associated with the CdTe material, in the visible-infrared (V-IR) range, and a Plasmon resonance in the ultraviolet (UV). In the three energy ranges: (4.87 - 5.47 eV), (6.26 - 12.72 eV) and (14.23−14.80 eV), ε1(ω) becomes negative. The first and main peaks of ε2(ω) are observed, respectively, at energies 1.85 eV and 4.68 eV. The ZnTe possesses a Mie resonance in the infrared-ultraviolet (IR-UV) range and a Plasmon resonance in the ultraviolet (UV). In the (5.21-5.77 eV) and (6.22 -16.04 eV) energy intervals, ε1(ω) changes to a negative sign. The first and main peaks of ε2(ω) appear respectively at energies 2.68 eV and 4.90 eV. For the ternary alloy Hg 1-x Cd x Te, (x = 0.25), the Mie resonance is located in the far-infrared- short-wave infrared (FIR-SWIR) range. However, the Plasmon resonance is found in the ultraviolet (UV) zone. ε1(ω) changes sign in the energy range (6.15 - 14.64 eV). The first peak and the main peak of ε2(ω) are observed, respectively, at 0.26 eV and 2.18 eV. For the case of x = 0.5, the Mie resonance is observed in the Far Infrared- short-wave Infrared (FIR-SWIR) range. However, the Plasmon resonance shows up in the Ultraviolet (UV) range. Negative values of ε1(ω) are observed in the energy interval (6.19 - 14.98 eV). The first and main peaks of ε2(ω) correspond, respectively, to 0.67 eV and 2.26 eV. For x = 0.75 the Mie resonance is found in the whole infrared (IR) range, and the Plasmon resonance is located in the ultraviolet (UV) range. ε1(ω) changes sign in two energy ranges: (5.09 - 5.51 eV) and (6.22 - 15.19 eV). The energies associated with the first and main peaks of the imaginary part ε2(ω) are found at 1.39 eV and 4.90 eV, respectively. For the second ternary alloy Hg0.5Zn0.5Te, and for X = 0.25 concentration, the Mie resonance is found in the Far infrared- short-wave infrared (FIR-SWIR) region and the Plasmon resonance in the ultraviolet (UV). The real part of ε1(ω), shifts to negative values in the region (6.22 - 14.64 eV). The first and main peaks of ε2(ω), are found at 0.30 eV and 2.03 eV, respectively. For X = 0.5, the material shows a Mie resonance in the Far-infrared- near-infrared (FIR-NIR) region and a Plas-mon resonance in the ultraviolet C (UVC). In the energy range (6.15 -15.59 eV), the real part of ε1(ω), becomes negative. The first and main peaks of ε2(ω), are found at 1.43 eV and 4.90 eV, respectively. For the case of X = 0.75, the Mie resonance is observed in the visible-infrared (V-IR) region, while the Plasmon resonance is found in the ultraviolet C (UVC). In the (5.09 -6 eV) and (6.22 - 15.74 eV) energy zones, the real part of the dielectric function shifts to negative values. The first and main peaks of ε2(ω) show up at energy 1.92 eV and 4.94 eV. The obtained results are in agreement with those reported in for the case of the Hg0.5Zn0.5Te alloy, and with those reported in for the ZnTe material. For Hg0.5Zn0.5Te, the results of dielectric function are in agreement with 15 except for X = 0.25 and 0.5, where the imaginary part spectrum differs slightly. In the literature, data regarding the optical properties of the studied materials have been scarce.

Figure 7 Spectrum of the real part of the dielectric function of Hg 1-x Cd x Te and Hg 1-x Zn x Te alloys for (x = 0, 0.25, 0.5, 0.75 and 1). 

Figure 8 Spectrum of the imaginary part of the dielectric function of Hg 1-x Cd x Te and Hg 1-x Zn x Te alloys for (x = 0, 0.25, 0.5, 0.75 and 1). 

The loss of electron’s energy, when moving in a given material, is defined by the energy loss function L(ω) given in Fig 9, for which the main peaks are associated with the Plasmon frequencies ωp (Eplasmon=Xωp, ωp14-36. For the binary materials HgTe, CdTe, and ZnTe, the first peaks of L(ω) are observed at 4.56 eV, 5.51 eV, and 7.87 eV, respectively. The main peaks are situated at 14.57 eV, 15.06 eV, and 17.29 eV, respectively. In the case of the ternary alloy , the first peaks of L(ω) appear at 4.41 eV, 5.62 eV and 5.73 eV for X = 0.25, 0.5, 0.75, respectively, while the main peaks are observed at 15.02 eV, 15.02 eV and 15.97 eV, respectively. The first peaks of Hg 1-x Cd x Te for X = 0.25, 0.5, and 0.75 appear at 4.41 eV, 5.92 eV, and 8.30 eV, respectively, while the main peaks are observed at 14.57 eV, 15.51 eV, and 15.78 eV, respectively. For each alloy and any energy less than the first peak energy, there is no loss of electron energy. For 𝑥=0, 0.25, 0.5, 0.75, and 1.0, the energies associated with the Plasmon frequencies are found to be greater than those cited in the work of Gang Wang et al., 37 in the case of Hg 1-x Cd x Te, and in the work of Qing-Fang Li et al., 38 for the ZnTe material. It should be reminded that, in these studies, the computation of the dielectric function was done for gap energies smaller than those used in our work. For HgTe, the results of L(ω) agree with the data reported in 39. For Hg 1-x Zn x Te, the energies associated with the main peaks of L(ω) are in good agreement with 15.

Figure 9 Energy loss function L(ω) of Hg 1-x Cd x Te and Hg 1-x Zn x Te alloys for (x = 0, 0.25, 0.5, 0.75 and 1) as a function of energy. 

The absorption coefficient α(ω) is related to the extinction coefficient K(ω) (5 and 7) and accounts for the average distance traveled by photons, before being absorbed in the material 35. For the binary alloys, absorption starts from energy values: 1.2 eV [HgTe], 1.85 eV [CdTe] and 2.68 eV [ZnTe]. It reaches maximal values at 6.30 eV [HgTe], 7.13 eV [CdTe] and 4.90 eV [ZnTe]. These results are comparable to those cited in 49. For the ternary alloy Hg 1-x Cd x Te (X=0.25, 0.5 and 0.75), the absorption starts at 1.58 eV, 1.43 eV and 1.77 eV, respectively. It reaches maximum values at 6.60 eV, 6.64 eV and 6.60 eV. In the case of the ternary alloy Hg 1-x Zn x Te (X = 0.25 0.5 and 0.75), the absorption starts at 1.20 eV, 1.85 eV and 2.34 eV, respectively. It becomes maximal at 6.30 eV, 6.68 eV, and 6.75 eV. Extinction coefficient and absorption coefficient spectrum are reported in Fig 10 and 11, respectively. The absorption coefficients relative to the ternary alloy Hg 1-x Cd x Te are found to agree with 15. For alloy, Hg 1-x Cd x Te the absorption coefficient spectrums, as reported in this work, are published for the first time and may constitute data to be compared within future works.

Figure 10 Extinction coefficient of Hg1-xCdxTe and Hg 1-x Zn x Te alloys for (x = 0, 0.25, 0.5, 0.75 and 1) as a function of energy. 

Figure 11 Absorption coefficient α (ω) of Hg 1-x Cd x Te and Hg 1-x Zn x Te alloys for (x = 0, 0.25, 0.5, 0.75, 1) as a function of energy. 

The refractive index n(ω) plot presented in Fig. 12 and that of the reflection coefficient R(ω) in Fig. 13 of the based HgTe ternary alloys shows a decreasing trend as a function of Cd and Zn concentrations. For a given frequency ω and for the binary materials: HgTe, CdTe, and ZnTe, the maximal values of the reflection coefficient fall into the Ultraviolet C (UVC) region. The same conclusion is valid for all concentrations X of Cd in the Hg 1-x Cd x Te and of Zn in the Hg 1-x Zn x Te materials.

Figure 12 Refractive index of Hg 1-x Cd x Te and Hg 1-x Zn x Te alloys for (x = 0, 0.25, 0.5, 0.75 and 1) as a function of energy. 

Figure 13 Reflectivity R(ω) of Hg 1-x Cd x Te and Hg 1-x Zn x Te alloys for (x = 0, 0.25, 0.5, 0.75 and 1) as a function of energy. 

The refractive index n(ω), the reflection coefficient R(ω), and the static value ε1(0), associated with different alloys, are reported in Table VI and are represented, in Fig. 14, as functions of concentration x. The values of ε1(0) for CdTe, ZnTe, and Hg0.25Cd0.75Te are in agreement with the results of other theoretical works; however, for HgTe, ZnTe, Hg0.75Cd0.25Te and Hg0.5Cd0.5Te materials ε1(0) differ sensibly from the results reported in . It should be noted that for CdTe and ZnTe, the values of ε1(0) are in disagreement with the experimental results in Ref. 46 47. The calculated refractive index is in good agreement with other theoretical 29-31 and experimental 40-41-47 results for HgTe, CdTe, Hg0.5Cd0.5Te and Hg1-xZnxTe (for X = 0.25, 0.5 and 0.75). For ZnTe, the value of n(0) is in agreement with other theoretical results 31 but differs from the experimental data 40. Since no theoretical or experimental studies have been carried out on the optical properties, namely refractive index and reflection index of Hg0.75Cd0.25Te and Hg0.25Cd0.75Te, no conclusions can be drawn on the validity of our results, for they are still open to experimental verification.

Table VI Static dielectric function ε1(0), refractive index n(0) and reflectivity R(0) of Hg 1-x Cd x Te and Hg 1-x Zn x Te alloys, using TB-mBJLDA potential. 

Alloys ε1(0) n(0) R(0)
Material This work Other works This work This work Other works
Theoritical Experimental Theorital Experimental
Binary HgTe 15.85 16.9d,15,35j 3.98 3.7e 4.51g 0.358 0.374a
CdTe 6.27 6.7c 10.31f 2.50 2.55e 3.26h 0.184 -
ZnTe 6.65 6.75b, 7.1j 9.63h 2.58 2.5b 4.5g 0.194 -
x=0.25 11.93 15.35c - 3.45 3.30e 0.303 -
Hg1−xCdxTe x=0.5 8.62 10,41c - 2.93 3.00e 3.13i 0.242 -
x=0.75 7.25 7.53c - 2.69 2.74e 0.210 -
Tenary x=0.25 11.71 - - 3.422 - - 0.300 -
Hg1−xZnxTe x=0.5 8.36 - - 2.892 - - 0.236 -
x=0.75 7.37 - - 2.716 - - 0.213 -

Figure 14 Variation of the dielectric constant, the refractive index and the reflectivity of Hg 1-x Cd x Te and Hg 1-x Zn x Te alloys as a function of concentration x at (ω = 0). 

4.Conclusion

In summary, the structural, electronic, and optical properties of Hg 1-x Zn x Te and Hg 1-x Zn x Te alloys were investigated using the full-potential linearized augmented plane wave (FP-LAPW). The study of structural properties of Hg 1-x Zn x Te and Hg 1-x Zn x Te materials, as done in this work, has confirmed that results obtained by the LDA approximation are better than those obtained by the GGA approach. The bulk modulus of Hg 1-x Zn x Te is greater than those of Hg 1-x Zn x Te alloys. The gap energies deduced from the band structures are underestimated by the LDA and the GGA for the two ternary alloys; however, they compare well to the experimental results when the mBJ-LDA potential is used. The same potential mBJ-LDA gives different values of gaps depending on the use of the lattice parameter aLDA calculated by the LDA approximation, or the use of the lattice parameter aGGA calculated by the GGA approximation. For all alloys, the coupling of mBJ-LDA potential with the lattice parameter aGGA, gives better results except for the case of Hg0.5Zn0.5Te and Hg0.25Zn0.75Te, where the use of the lattice parameter aLDA is preferable. For the binary and ternary alloys, the electronic properties, evaluated under either the LDA, GGA, or TB-mBJLDA potential schemes, are found to be those of semiconductors with direct band gaps at the Γ-point. The critical points of the optical constant spectrum (first peaks, main peaks, etc.) calculated from the dielectric function of Hg 1-x Zn x Te and Hg 1-x Zn x Te alloys are distinct. This distinction can be attributed to the difference in gap energies and the nature of the elements composing the different materials. In conclusion, one can say that the two ternary alloys possess comparable optical properties (refractive index, dielectric constant, and reflectivity). Results relative to the optical properties of the studied compounds could bear practical importance; especially, in applications such as microelectronic, optoelectronic, solar cell, and nuclear systems.

References

1. D. R. Yakovlev and W. Ossau, Magnetic Polarons, in Introducction to the Physics of Diluted Magnetic Semiconductors, edited by J. Kossut and J. A. Gaj(Springer-Verlag, Berlin, 2010); pp 18-19. DOI 10.1007/978-3-642-15856-8 [ Links ]

2. ESPI Metals. Mercury Zinc Telluride (HgZnTe) Semiconductors. AZoM. https://www.azom.com/article.aspx?ArticleID=8467 . viewed 20 November 2019. [ Links ]

3. M. Diakides, J. D. Bronzino, and D. R. Peterson, eds. Medical infrared imaging: principles and practices. (CRC press, 2012). https://doi.org/10.1201/b12938pp1.1-1.15 [ Links ]

4. Williams, Philip C, and Susan G. Stevensen. Near-infrared reflectance analysis: food industry applications. Trends Food Sci. Technol. 1 (1990) 44. https://doi.org/10.1016/0924-2244(90)90030-3 [ Links ]

5. R. R. Hampton, Applied Infrared Spectroscopy in the Rubber Industry, Rubber Chem. Technol. 45(1972) 46, https://doi.org/10.5254/1.3544726 [ Links ]

6. C. Corsi, Infrared: A Key Technology for Security Systems, Adv. Opt. Technol. vol. 2012, Article ID 838752, (2012). https://doi.org/10.1155/2012/838752 [ Links ]

7. R.S. Hansen , Modeling of the nonlinear response of the intrinsic HgCdTe photoconductor by a two-level rate equation with a finite number of carriers available for photoexcitation, Appl.Opt. 42 (2003) 4819. doi: 10.1364/ao.42.004819. [ Links ]

8. N. Romeo V. Canevari L. Zini C. Spaggiari, HgCdTe thin films for solar cells application prepared by multisource evaporation, Thin Solid Films, 157 (1988) 175. https://doi.org/10.1016/0040-6090(88)90001-6 [ Links ]

9. Rogalski, Antony. HgCdTe infrared detector material: history, status and outlook. Rep. Prog. Phys. 68 (2005) 2267.url: https://doi.org/10.1088/0034-4885/68/10/R01 [ Links ]

10. A. Rogalski, Hg 1-x ZxTe As a potential infrared detector material Prog. Quant. Electr. 13 (1989) 299. https://doi.org/10.1016/0079-6727(89)90008-6 [ Links ]

11. M. Boucharef, et al. First-principles study of the electronic and structural properties of (CdTe) n/(ZnTe) n superlattices. Superlattices Microstruct. 75 (2014) 818. https://doi.org/10.1016/j.spmi.2014.09.014 [ Links ]

12. F. Hassan, El Haj, et al. Ab initio study of the fundamental properties of HgSe, HgTe and their HgSexTe 1-x alloys. Phys. Scr 84.6 (2011) 065601. https://doi.org/10.1088/0031-8949/84/06/065601 [ Links ]

13. M. Debbarma et al., Density Functional Calculations of Elastic and Thermal Properties of Zinc-Blende Mercury-Cadmium-Chalcogenide Ternary Alloys. Met. Mater. Int. (2020). https://doi.org/10.1007/s12540-020-00778-7 [ Links ]

14. F. Kadari, et al. First-principles study of the structural, electronic and optical properties of the cubic triangular quaternary ZnxCdyHg 1-x-y Te alloys under hydrostatic pressure. Chin. J. Phys. 59 (2019) 209. https://doi.org/10.1016/j.cjph.2019.02.016 [ Links ]

15. A. Laref, et al. Compositional and spin-orbit control on the electronic structure and optical characteristics of Zn-HgTe alloys using mBJ-GGA approach. J. Mater. Sci. 52.12 (2017) 7039-7057. https://doi.org/10.1007/s10853-017-0937-5 [ Links ]

16. S. Al-Rajoub, and B. Hamad, Theoretical investigations of the structural, electronic and optical properties of Hg1-x Cd x Te alloys. Philos Mag. 95.22 (2015) 2466-2481.https://doi.org/10.1080/14786435.2015.1061219 [ Links ]

17. B.V. Robouch et al., Ion distribution preferences in ternary crystals Zn x Cd 1-x Te, Zn 1-x Hg x Te and Cd 1-x Hg x Te. Eur. Phys. J. B 84.2(2011) 183-195. https://doi.org/10.1140/epjb/e2011-20575-1 [ Links ]

18. A. Morales-García, R. Valero, and F. Illas, An empirical, yet practical way to predict the band gap in solids by using density functional band structure calculations. J. Phys. Chem C. 121 (2017): 18862-18866. 10.1021/acs.jpcc.7b07421. [ Links ]

19. S. Belhadj, B. Lagoun, M. Benabdallah Taouti, S. Khenchoul, A. Benghia, and D. Benbertal. TB-mBJ calculation of structural, electronic and optical properties of two monovalent iodates AIO3 (A= Tl, a-Rb). Chin. J. Phys. 59 (2019) 10-20. https://doi.org/10.1016/j.cjph.2019.02.019 [ Links ]

20. J. A. Camargo-Martínez, and R. Baquero, Performance of the modified Becke-Johnson potential for semiconductors. Phys. Rev. B. 86.19 (2012) 195106. https://doi.org/10.1103/PhysRevB.86.195106 [ Links ]

21. D. Koller, F. Tran, and P. Blaha, Merits and limits of the modified Becke-Johnson exchange potential Phys. Rev. B. 83.19 (2011) 195134. https://doi.org/10.1103/PhysRevB.83.195134 [ Links ]

22. T. Takeda, Linear methods for fully relativistic energy-band calculations. J. Phys. F: Met. Phys. 9.5 (1979) 815. https://doi.org/10.1088/0305-4608/9/5/009 [ Links ]

23. Elk version 5.2.14, http://elk.sourceforge.net/. [ Links ]

24. J. P. Perdew, E. R. McMullen, and Alex Zunger, Densityfunctional theory of the correlation energy in atoms and ions:a simple analytic model and a challenge. Phys. Rev. A. 23.6 (1981) 2785. https://doi.org/10.1103/PhysRevA.23.2785 [ Links ]

25. Perdew, John P., Kieron Burke, and Matthias Ernzerhof. Generalized gradient approximation made simple. Phys. Rev. Lett. 77.18 (1996) 3865. https://doi.org/10.1103/PhysRevLett.77.3865 [ Links ]

26. Meinert, Markus. Modified Becke-Johnson potential investigation of half-metallic Heusler compounds. Phys. Rev.B. 87.4 (2013) 045103. https://doi.org/10.1103/PhysRevB.87.045103 [ Links ]

27. Marques, Miguel AL, Micael JT Oliveira, and Tobias Burnus. Libxc: A library of exchange and correlation functionals for density functional theory. Comput. Phys. Commun.183.10 (2012) 2272. https://doi.org/10.1016/j.cpc.2012.05.007 [ Links ]

28. Birch, Francis. Finite elastic strain of cubic crystals. Phys. Rev. 71.11 (1947) 809. https://doi.org/10.1103/PhysRev.71.809 [ Links ]

29. San-Dong, Guo, and Liu Bang-Gui. Density-functional theory investigation of energy gaps and optical properties of Hg1-xCdxTe and In1-xGaxAs. Chin. Phys. B. 21.1 (2012) 017101. https://doi.org/10.1088/1674-1056/21/1/017101 [ Links ]

30. Qi-Jun, Liu, Zhang Ning-Chao, Liu Fu-Sheng, and Liu Zheng-Tang. Structural, electronic, optical, elastic properties and Born effective charges of monoclinic HfO2 from first-principles calculations. Chin. Phys. B. 23, no. 4 (2014): 047101.https://doi.org/10.1088/1674-1056/23/4/047101 [ Links ]

31. Korozlu, Nurettin, K. Colakoglu, and E. Deligoz. Structural, electronic, elastic and optical properties of cdxzn1-xte mixed crystals. Journal of Physics: Condensed Matter 21.17 (2009) 175406. https://doi.org/10.1088/0953-8984/21/17/175406 [ Links ]

32. Ilyas, Bahaa M., and Badal H. Elias. A theoretical study of perovskiteCsXCl3 (X= Pb, Cd) within first principles calculations. Physica B Condens 510 (2017) 60-73.https://doi.org/10.1016/j.physb.2016.12.019 [ Links ]

33. Zaari, H., M. Boujnah, A. El Hachimi, A. Benyoussef, and A. El Kenz. Optical properties of ZnTe doped with transition metals (Ti, Cr and Mn).Opt Quant Electron. 46(2014) 75-86. https://doi.org/10.1007/s11082-013-9708-y [ Links ]

34. Toudert, Johann, and Rosalía Serna. Interband transitions in semi-metals, semiconductors, and topological insulators: a new driving force for plasmonics and nanophotonics. Opt.Mater. Express. 7 (2017) 2299-2325. https://doi.org/10.1364/OME.7.002299 [ Links ]

35. Ali, M. A., M. Anwar Hossain, M. A. Rayhan, M. M. Hossain, M. M. Uddin, Md Roknuzzaman, Ken Ostrikov,A. K. M. A. Islam, and S. H. Naqib. First-principles study of elastic, electronic, optical and thermoelectric properties of newly synthesized K2Cu2GeS4 chalcogenide. J. Alloys Compd. 781: 37-46(2019). https://doi.org/10.1016/j.jallcom.2018.12.035 [ Links ]

36. Mendi, R. Taghavi, S. M. Elahi, and M. R. Abolhassani. Firstprinciples investigation of the structural, electronic and optical properties of V-doped single-walled ZnO nanotube (8, 0).MOD PHYS LETT B. 28.17: 1450139(2014). https://doi.org/10.1142/S0217984914501395 [ Links ]

37. Wang, Gang, Song Wu, Zhaohua Geng, Songyou Wang, Liangyao Chen, and Yu Jia. First-principles study on the electronic structures and the optical properties of Hg 1-x Cd x Te. J KOREAN PHYS SOC. 56, no. 41: 1307-1310(2010). DOI: 10.3938/jkps.56.1307 [ Links ]

38. Li, Qing-Fang, Ge Hu, Qing She, Jing Yao, and Wen-Jiang Feng. Electronic structure and optical properties of Cudoping and Zn vacancy impurities in ZnTe.,J Mol Model. 19, no. 9: 3805-3812(2013). https://doi.org/10.1007/s00894-013-1901-1 [ Links ]

39. Secuk, M. N., M. Aycibin, B. Erdinc, S. E. Gulebaglan, E. K. Dogan, and H. Akkus. Ab-initio calculations of structural, electronic, optical, dynamic and thermodynamic properties of HgTe and HgSe. Am J. Condens. Matter Phys. 4, no. 1: 13-19(2014). DOI: 10.5923/j.ajcmp.20140401.02 [ Links ]

40. Ireneusz Strzalkowski, Sharad Joshi, and C. R. Crowell [1976 APPL PHYS LETT. 28 350.40] Cardona, Manuel. Infrared dielectric constant and ultraviolet optical properties of solids with diamond, zinc blende, wurtzite, and rocksalt structure. J. Appl Phys. 36.7 (1965) 2181. https://doi.org/10.1063/1.1714445 [ Links ]

41. E. Salman, and W. Al-zubady, Optical confinement factor of Hg0:2Cd0:8Te/ Hg0:5Cd0:5 Te multiple quantum well laser. College of Science for women/ University of Baghdad (2018). [ Links ]

42. Tedjini, M. H., A. Oukebdane, M. N. Belkaid, N. Aouail, and N. Belameiri. Ab initio and Monte Carlo studies of physical properties of semiconductor radiation detectors. Indian J. Phys. (2021) 1-12. https://doi.org/10.1007/s12648-020-01916-y [ Links ]

43. Deligoz, Engin, Kemal Colakoglu, and Yasemin Ciftci. Elastic, electronic, and lattice dynamical properties of CdS, CdSe, and CdTe. Physica B Condens 373 (2006) 124-130. https://doi.org/10.1016/j.physb.2005.11.099 [ Links ]

44. Woolley, J. C., and B. Ray. Solid solution in AIIBVI tellurides. Journal of Physics and Chemistry of Solids 13.1-2(1960) 151-153. https://doi.org/10.1016/0022-3697(60)90135-9 [ Links ]

45. S. Adachi, Properties of Group-IV, III-V and II-VI Semiconductor, John Wiley and Sons Ltd, The Atrium, Southern Gate, Chichester, West Sussex PO19 8SQ, England, 2005. 978-0-470-09032-9. [ Links ]

46. Ireneusz Strzalkowski, Sharad Joshi, and C. R. Crowell, Dielectric constant and its temperature dependence for GaAs, CdTe, and ZnSe, Appl. Phys. Lett. 28(1976) 350. doi: 10.1063/1.88755 [ Links ]

47. T. Hattori, Y. Homma, A. Mitsuishi, and M. Tacke. Indices of refraction of ZnS, ZnSe, ZnTe, CdS, and CdTe in the far infrared. Opt. Commun. 7(1973) 229-232. https://doi.org/10.1016/0030-4018(73)90015-1 [ Links ]

48. R. Khenata, A. Bouhemadou, M. Sahnoun, Ali H. Reshak, H. Baltache, and M. Rabah, Elastic, electronic and optical properties of ZnS, ZnSe and ZnTe under pressure. Comput. Mater. Sci. 38(2006) 29. https://doi.org/10.1016/j.commatsci.2006.01.013 [ Links ]

49. M. Cardona, and G˜A Hunther Harbeke, Absorption Spectrum of Germanium and Zinc Blende Type Materials at Energies Higher than the Fundamental Absorption Edge. J. Appl. Phys. 34(1963) 813. https://doi.org/10.1063/1.1729543 [ Links ]

50. Ghasemi Hasan, Mokhtari Aliand Soleimanian Vishtasb, Introduce of ZnxHg(1-x)Te as a room temperature photodetector: ab initio calculations of the electronic structure and charge carrier transport, Mater. Res. Express. 5 (2018). 015910 https://doi.org/10.1088/2053-1591/aaa740 [ Links ]

51. L. Ley, R. A. Pollak, F. R. McFeely, Sa P. Kowalczyk, and D. A. Shirley, Total valence-band densities of states of III-V and II-VI compounds from X-ray photoemission spectroscopy. Phys. Rev. B 9 (1974) 600. https://doi.org/10.1103/PhysRevB.9.600 [ Links ]

52. F. Boutaiba, Ali Zaoui, and M. Ferhat. Fundamental and transport properties of ZnX, CdX and HgX (X= S, Se, Te) compounds. Superlattice Microst 46.6 (2009) 823. https://doi.org/10.1016/j.spmi.2009.09.002 [ Links ]

53. M. Debbarma, B. Debnath, D. Ghosh, S. Chanda, R. Bhattacharjee, and S. Chattopadhyaya, First principle based calculations of the optoelectronic features of HgSxSe1-x, HgSxTe1-x and HgSexTe1-x alloys with GGA+ U functional. J. Phys. Chem. Solids 131(2019) 86. https://doi.org/10.1016/j.jpcs.2019.03.009 [ Links ]

54. M. Linder, GF Schatz, P. Link, HP Wagner, W. Kuhn, and W. Gebhardt, J. Phys. Condens. Matter 4(1992) 4601. [ Links ]

55. Hansen, G. L, J. L. Schmit, and T. N. Casselman. Energy gap versus alloy composition and temperature in Hg 1-x CdxTe. J. Appl. Phys. 53 (1982) 7099. https://doi.org/10.1063/1.330018 [ Links ]

56. Miloua, R., Z. Kebbab, F. Miloua, and N. Benramdane. Ab initio investigation of phase separation in Ca 1-x Z n-x O alloys. Phys. Lett. A372 (2008) 1910. https://doi.org/10.1016/j.physleta.2007.10.077 [ Links ]

57. O. Madelung, W. Von der Osten, and U. Rössler, Intrinsic Properties of Group IV Elements and III-V, II-VI and I-VII Compounds/Intrinsische Eigenschaften Von Elementen Der IV. Gruppe und Von III-V-, II-VI-und I-VII-Verbindungen. Vol. 22.Springer Science & Business Media, 1986. [ Links ]

58. M. B. Reine, Fundamental properties of mercury cadmium telluride. Encyclopedia of Modern Optics, Academic Press, London 322(2004). [ Links ]

59. K. H. Hellwege, and O. Madelung , Semiconductors Physics of Group IV Elements and III-V Compounds. Landolt-Börnstein New Series, Group III 17 (1982). [ Links ]

60. Okuyama, Hiroyuki, Yuko Kishita, and Akira Ishibashi. Quaternary alloy Zn 1-x MgxS y Se 1-y . textit Phys. Rev. B 57(1998) 2257. https://doi.org/10.1103/PhysRevB.57.2257 [ Links ]

Received: January 11, 2021; Accepted: March 16, 2021