Investigación

Self-focusing in chromium-doped potassium niobate single ceramic crystal

J. Castillo-Torresª*, J. Hernández A.^b**, S. González-Martínezª, A. Aguirre-Lópezª, M. B. Hernándezª, and J.A. Aguilar-Martínezª

ª Instituto de Física y Matemáticas, Universidad Tecnológica de la Mixteca, 069000, Huajuapan de León, Oaxaca, México, e-mail: jaimec@mixteco.utm.mx*

^b Instituto de Física, Universidad Nacional Autónoma de México, PO Box 20-364, 01000 México, D.F, México,
e-mail: josemh@fisica.unam.mx**

Recibido el 23 de agosto de 2006
Aceptado el 26 de octubre de 2006

Abstract

The self-focusing and nonlinear optical absorption in a chromium-doped potassium niobate single ceramic crystal have been investigated. The third-order electric susceptibility χ⁽³⁾ at continuous 532 nm radiation is estimated based on a band transport model describing photorefractive properties for this electro-optic material. An anisotropic behavior on its nonlinear optical absorption properties has also been observed due to the presence of chromium ions.

Keywords: Self-focusing; nonlinear electric susceptibility.

Resumen

Se investigo el auto-enfocamiento y la absorción óptica no lineal en un cristal cerámico de niobato de potasio dopado con cromo. Se estimó el valor de la susceptibilidad electrica a tercer orden χ⁽³⁾ para una radiación continua de 532 nm sobre la base de un modelo de transporte de banda que describe las propiedades fotorefractivas para este material electro-óptico. También se observó un comportamiento anisótropo en sus propiedades ópticas no lineales debido a la presencia de iones de cromo.

Descriptores: Auto-enfocamiento; susceptibilidad eléctrica no lineal.

PACS: 78.20.Ci; 77.84.Dy

DESCARGAR ARTÍCULO EN FORMATO PDF

Acknowledgements

J. Castillo-Torres acknowledges with gratitude the financial support by Grant CONACYT (México) No. 46833. The authors also wish to thank Dr. C. Medrano for the crystals samples supplied.

References

1. M. Segev, B. Crosignani, A. Yariv, and B. Fisher, Phys. Rev. Lett. 68 (1992) 923.        [ Links ]

2. W. Królikowski, B. Luther-Davies, and C. Denz, IEEE J. Quantum Electron. 39 (2003) 3.        [ Links ]

3. M. Sheik-Bahae, A.A. Said, T.H. Wei, D.J. Hagan, and E.W.V. Stryland, IEEE J. Quantum Electron. 26 (1990) 760.        [ Links ]

4. N.V. Kukhtarev, V.B. Markov, S.G. Odulov, M.S. Soskin, and V.L. Vinetskii, Ferroelectrics 22 (1979) 949.        [ Links ]

5. W. Xing, H. Looser, H. Wuest, and H. Arend, J. Cryst. Growth 78 (1986) 431.        [ Links ]

6. F. Agulló-López, C.R.A. Catlow, and P.D. Townsend, Point Defects in Materials (Academic Press, London, 1988) p. 119.        [ Links ]

7. J. Castillo-Torres, J. Hernández A., C. Medrano P., E. Camarillo G., and H. Murrieta S., Opt. Mat. 22 (2003) 251.        [ Links ]

8. S.Q. Wang Song, Ch. P Zhang, and P.J. Talbot, Opt. Commun. 98 (1993) 269.        [ Links ]

9. P. Xie, I. Taj, and T. Mishima, J. Opt. Soc. Am. B 18 (2001) 479.        [ Links ]

10. R. de Nalda et al., J. Opt. Soc. Am. B 19 (2002) 289.        [ Links ]

11. H.P Li, C.H. Kam, Y.L. Lam and W. Ji, Opt. Mat. 15 (2001)        [ Links ]

12. R. Ryf, A. Lötscher, C. Bosshard, M. Zgonik, and P. Günter, J. Opt. Soc. Am. B 15 (1998) 989.        [ Links ]